Is the blade ready for stropping?

I always start after my finest stone. Sometimes I quit after 1000 diamond, sometimes I go to 3k or 10k chosera.

Nicholas, I am interested in your progression. Do you find it works better alternating between the stones and balsa strops? Have you tried going to 1000 diamonds before stropping?

What difference do you see between the balsa and leather?

I use the WE diamond stones and 14/10 diamond paste on balsa strops and 5/3.5 diamond paste on leather strops. What I found, that works for me, is I sharpen with the 600 grit diamond stones and move up to 14 micron paste on balsa, then move back to the 800 grit diamond stones, then 10 micron paste on balsa, then I finish the edge on 1000 grit diamond stones. Once i’m happy with the edge I lower the angle by a degree or two and progress to polishing using the 5/3.5 diamond pastes on leather strops till i have a mirror polish. The wicked edge knife sharpener website has a detailed list of every stone and diamond paste/spray and images of scratch patterns under resources, labelled grit comparison chart. It helped me to determine the stone/grit sequence for sharpening.

Nicholas,
This has come up many times on the WEPS boards. The common wisdom here, and advice I have given is to go through all of your stones and then strop. Looking at grit scratch patterns does not neccessarily tell you what is happening at the edge with different media. Give it a try and see what you think. The beauty of the WEPS is that you can easily experiment.

Something to think about. Stropping will give a bit of a convex profile to the edge of the edge. Balsa less so than leather, but it still does it. When you switch back to a stone after stropping, you need to remove that convex shoulder before you get to the edge again. You are working against yourself by switching back and forth.

Phil

Phil, Thanks for the thought. Right back at you, just a thought, we’re going to strop anyways causing the bevel edges to convex anyways….. In the past I found I spent too much time stropping after the stone to obtain a mirror polish causing the bevel to convex and affect my edge. This saved me a lot of time and the polish was great, but I did baby it 🙂

Nicholas,
I am a great proponent of doing what works for you. I never tend to argue with success. Still I would like to make some comments on this, from the logical point of view as well as my personal experience with the WEPS.

First, if you spend too much time using strops to remove scratches, you need finer stones. The pastes and sprays that we use on our strops just do not have the abrasive concentration that stones do, meaning the are slower and less efficient at scratch removal. Depending on the scratch width and depth, it is not practical to get rid of them with strops. Typically stropping is used for final polish and edge refinement, not scratch removal. Of course there are exceptions. Ken Schwartz sell some sprays with 30 micron abrasives and more in them. With these abrasives on a hard media like nanocloth. perhaps scratch removal is more in reach.

Second, I am not sure if I communicated well about the different effects of the strops and stones and why they sort of cancel each other out when you alternate them. Consider that the stones in theory give you a nice V at the edge. The strops add a convex shoulder below the edge of the edge. When you go from stones to strops, you put the convex on the edge. When you go back to the stones, you must remove the convex shoulder before you get back to that perfect V. Now, this just does not seem very efficient. There must be a reason that folks that have lots of experience with the WEPS do not recommend this.

Third, If your are truly rounding your edge with the strops, you might examine your stropping technique. Try reducing the angle a bit, or reducing the number of strokes, or lightening up on the pressure. This will not get scratches removed, but, again, at this level you shoudn’t be trying to remove much in the way of scratches anyway.

Again, if what you are doing makes you happy, have at it. I am simply offering some of my experience… hard won at the expense of litteraly hundreds of hours sharpening on the WEPS. I have tried many, many different things. The way I use my WEPS now is way different than when I got it. However, I am still learning.

BTW One other thing to try as well… go through all of your stones and then strops, go back to something like the 1200 grit ceramics (or 1000 grit stones if that is what you heve) increase your angle by a degree or two and make a half dozen or so very light passes on the edge. If you have over stropped and rounded your edge, this should fix it. It also adds back some of the tooth and bite that stropping and/or the use of very fine stones removes.

Phil

BTW One other thing to try as well… go through all of your stones and then strops, go back to something like the 1200 grit ceramics (or 1000 grit stones if that is what you heve) increase your angle by a degree or two and make a half dozen or so very light passes on the edge. If you have over stropped and rounded your edge, this should fix it. It also adds back some of the tooth and bite that stropping and/or the use of very fine stones removes.

Phil

Phil, I just read your post above AFTER the question I just posted this morning about stropping that was linked to the post I just made on the Buck 450 recent sharpening………..I think you may have answered my question right here perfectly ! One question on this though……when you say to ” increase the angle by a degree “, should I do that by sliding the arms out on the angle rod, or should I use the micro-fine adjustment screw on the arms, and if so, what would a degree be on that adjustment screw, a full 360 turn or what ? ( as it is hard to use the angle cube and measure a single degree…..at least in my rather limited experience ) Thanks for any help for this newb trying to learn all he can ! :woohoo:

Phil, I just read your post above AFTER the question I just posted this morning about stropping that was linked to the post I just made on the Buck 450 recent sharpening………..I think you may have answered my question right here perfectly ! One question on this though……when you say to ” increase the angle by a degree “, should I do that by sliding the arms out on the angle rod, or should I use the micro-fine adjustment screw on the arms, and if so, what would a degree be on that adjustment screw, a full 360 turn or what ? ( as it is hard to use the angle cube and measure a single degree…..at least in my rather limited experience ) Thanks for any help for this newb trying to learn all he can ! :woohoo:

Darrell,
Do you have an angle cube? I use that device t set the angles. I guess it does not matter which method you use to change the angle. Of course the micro adjustments are easier to work with. Typically I start the setup with the micro adjustments centered in their travel so I have the max +/- adjustment available. I change angles of a degree or more using the adjustments made by moving the slider on the base bar. I don’t think there would be anything wrong with leaving the slider in place and calibrating the amount or turns of the micro adjustments required to get your desired amount of angle change. I would have to check, but I don’t think I get a full degree in either direction on the micro adjustments from their centered position.

The amount that you decrease the angle is really dependent on your stropping technique as well. If you, like Eamon, (and myself) use very light strokes, you may get away with a half degree decrease in angle. OTH, if you are stropping as Clay has described, with alcohol on the strops and lifting the base up with each stroke, you may want to decrease the angle by 2 degrees or more. The thing that you are trying to do is to finesse and refine the edge without rounding it. This becomes a balancing act of sorts. The key, after you understand the concept, is to try some different things and see what is working for you. My feather light is not likely identical to the pressure you would describe with the same term. As it is the interaction between the compliance of the stropping substrate, the amount of pressure used, and the angle, it would be difficult to set any sort of absolute rules for this.

Keep in mind the material compliance or give. The change in angle would be slightly different for leather versus balsa, or Kangaroo. Respectively they would require a descending amount of angle change. With nanocloth strops, I don’t change the angle from my primary angle at all.

I hope that this helps!
🙂